Transparencies produced from epoxy resins cured with adducts of boroxines and interlayers of mercaptan resins

ABSTRACT

A high heat resistant transparency of epoxy resins cured with adducts of trimethoxyboroxine and benzyl alcohol is disclosed to resist intense heat for these transparencies in their use on military and industrial hardware. Additionally, the transparency may include phosphite or phosphate compounds to improve heat resistance, with the phosphate compound in sufficient concentrations to delay gel times such that the phenyl substituted alkyl alcohol may be eliminated from the composition. This transparency may exist in a composite with other layers of transparent material known to those skilled in the art. The epoxy transparency layer is bound to the other transparent layers, in a variety of configurations, using an interlayer of mercaptan terminated resins. These resins greatly improve resistance to moisture permeability in and about the edges of the entire transparency.

CROSS-REFERENCE

This application is a continuation-in-part application of an application filed on Aug. 28, 1979, bearing Serial No. 70,390, issued Oct. 13, 1981 as Patent No. 4,294,886. This application is also a continuation-in-part application of an application filed on Nov. 6, 1980, bearing Serial No. 204,424, currently pending. Application Serial No. 204,424 is a continuation-in-part of application Serial No. 70,390.

TECHNICAL FIELD

This invention relates to the production of heat resistant transparencies and laminates including a heat resistant transparency layer. The layers may be adhered by resins resistant to moisture permeation to produce the laminate. Heat resistance may be enhanced by organic phosphorus compounds.

BACKGROUND ART

Heretofore, the use of transparencies in military and industrial hardware has required exacting properties for their certified use. For example, a military helicopter having vast areas of transparent material will require special transparent material having identifiable indices of refraction to prevent internal reflection of sunlight. Other transparencies require resistance to penetration by projectiles. Still other transparencies are designed for resistance to abrasion.

The use of these transparencies in military and industrial applications have been severely limited by the temperatures these composite materials could withstand. Direct application of a heat source or a high enegy point of origin could quickly alter the physical properties of the composite materials. Whether the thermal effects be generated by fossil fuel fires or laser application, the conventional transparencies lacked sufficient resistance to the intense heat generated. Therefore, the need exists for a material which is heat resistant, in order to complement the impact, ballistic, abrasion, or light resistant materials presently existing in composite transparencies.

Likewise, the use of these transparencies in military and industrial application has been subjected to irreversible damage caused by the penetration of moisture into the various layers of the composite transparent structure. The susceptibility of these materials to moisture penetration in humid conditions creates a lasting haze within the transparency structure. Further, the materials must maintain adhesion among the various layers and also must maintain modulus values among the various layers at acceptable and constant levels. Therefore, the need exists for a material which is resistant to moisture permeability to protect conventional and heat resistant transparent materials from haze characteristics but further maintains ultimate strength and constant modulus.

DISCLOSURE OF INVENTION

Therefore, it is an object of the invention to provide a transparency produced from epoxy resins cured with adducts of trimethoxyboroxine and benzyl alcohol to provide an intense heat resistant material to be incorporated with composite transparencies for use in military and industrial applications.

It is another object of the invention to provide a transparency produced from epoxy resins, as above, wherein the intense heat resistant material has the same or similar index of refraction in order that it be used with other composite materials to complement their properties.

Moreover, it is an object of the invention to provide transparencies produced from epoxy resins, as above, wherein the intense heat resistant material may control the reactivity of the entire transparency against degradation of properties caused by intense general heat or a high energized point source.

It is yet another object of the invention to provide a process for the production of transparencies having epoxy resins cured with adducts of trimethoxyboroxine and benzyl alcohol to insure intense heat resistant properties in the entire transparency.

Still another object of the invention is to provide a transparency produced from epoxy resins cured with adducts of trimethoxyboroxine and benzyl alcohol and triphenyl phosphite to improve the intense heat resistant characteristics of the transparent composite.

Yet another object of the invention is to provide a transparency produced from epoxy resins cured with adducts of trimethoxyboroxine and benzyl alcohol and triphenyl phosphite which can be formed into curved articles.

Another object of the invention is to provide a transparency produced from epoxy resins cured with adducts of boroxine compounds, phenyl-substituted alkyl alcohols and chlorophosphate compounds to improve the intense heat resistant characteristics of the transparency composite, which can also be formed into curved articles.

Still another object of the invention is to provide a transparency produced from epoxy resins cured with adducts of a boroxine compound and a chlorophosphate compound to improve the intense heat resistant characteristics of the transparent composite, which can also be formed into curved articles.

Another object of the invention is to provide a transparency produced from epoxy resins resistant to moisture permeability by the application of an interlayer binding means within the transparency composite.

Yet another object of the invention is to provide a mercaptan resin interlayer resistant to moisture permeability to protect transparent materials from the effects of moisture haze.

Still another object of the invention is to provide a mercaptan resin interlayer resistant to moisture permeability which maintains ultimate strength and modulus.

Still another object of the invention is to provide mercaptan resin edge sealer resistant to moisture permeability to protect transparent materials from the effects of moisture haze.

These, and other objects which will become more apparent as the detailed description of the preferred embodiment proceeds, are achieved by: a transparent composition having resistance to intense heat, comprising: a transparent blend having from 80 parts to about 100 parts of an epoxy resin; from 5.0 parts to about 30 parts of trimethoxyboroxine; and from 1 part to about 10 parts of a phenyl substituted alkyl alcohol. The objects also are achieved by: a transparency composition having resistance to intense heat, comprising: a transparent blend having from 80 parts to about 100 parts of an epoxy resin; from 5.0 parts to about 30 parts of trimethoxyboroxine; from 1 part to about 10 parts of a phenyl substituted alkyl alcohol; and from 5 parts to about 25 parts of a phosphite selected from the group consisting of diphenyl phosphite, trisnonylphenyl phosphite, triphenyl phosphite, diphenylisodecyl phosphite, dephenylisooctyl phosphite and phenyldiisodecyl phosphite.

The objects of the invention are also achieved by a blend having, (a) about 100 parts by weight of a mercaptan resin having the following formula: ##STR1## where R is an aliphatic hydrocarbon having from 1 to 18 carbon atoms, and where n is 1 or 2; (b) from about 40 to about 250 parts by weight of an epoxy resin; and (c) from about 0.5 parts by weight to about 4.0 parts by weight of a silane selected from the group consisting of:

N-aminoalkyl-aminoalkyl-trialkoxysilanes of the formula ##STR2## wherein R₁ is an alkylene having 1-6 carbon atoms and R₂ is an alkyl having 1-6 carbon atoms, and aminoalkyl-trialkoxysilanes of the formula ##STR3## wherein R₁ and R₂ are as defined above and combinations thereof.

The objects of the invention are also achieved by a composition resistant to moisture permeation, comprising: a transparent blend having a specific permeability of less than 1.00 mg. mm/24 hr cm² ; said blend comprising from about 100 parts by weight of a thio-terminated aliphatic hydrocarbon based resin; and from about 40 to about 250 parts by weight of an epoxy resin; and from about 0.5 parts by weight to about 4.0 parts by weight of a silane terminated compound.

The objects of the invention are further achieved by a transparent composition having resistance to intense heat, comprising: a transparent blend having (a) from about 80 to about 100 parts by weight of an epoxy resin; (b) from about 5 to about 30 parts by weight of a boroxine having the formula: ##STR4## where R is a compound having from 1 to 18 carbon atoms, and (c) from about 1 part to about 40 parts by weight of an organic phosphorus compound having the following formula: ##STR5## where R₃ is selected from the group consisting of hydrocarbon radicals having from 1 to 24 carbon atoms, halo-substituted organic radicals having from 1 to 24 carbon atoms, and multihalo-substituted organic radicals having from 1 to 24 carbon atoms; and where R₃ may be the same or different radicals;

where R₄ is selected from the group consisting of all the radicals of R₃, oxygen, and radicals of the formula: --O--R₆, where R₆ is selected from the group consisting of all the radicals of R₃, organo-phosphorus polymeric radicals, and organo-phosphorus esters; where R₅ is selected from the group consisting of hydrogen, hydroxyl, oxygen, sulfur, halogens or no radical at all; and where Z is selected from the group consisting of oxygen, sulfur, or no radical at all.

DESCRIPTION OF THE DRAWINGS

For an understanding of the invention, reference is had to the following drawings, wherein:

FIG. 1 is a cross sectional view of the transparency composite having the intense heat resistant interlayer;

FIG. 2 is a cross sectional view of the clad transparency composite having the intense heat resistant interlayer;

FIG. 3 is a graph of the production of the transparency having benzyl alcohol showing the increase in gel time;

FIG. 4 is a graph showing the effect of alcohol levels on the maximum exotherm in the reaction system;

FIG. 5 is a graph showing the increased burnthrough resistance on the transparencies having benzyl alcohol and triphenyl phosphite;

FIG. 6 is a graph showing the increased resistance to moisture permeability of mercaptan resin binding means bonded to various transparency layers when exposed to temperatures of about 200° F. and 100 percent relative humidity;

FIG. 7 is a graph showing the increased resistance to moisture permeability of mercaptan resin binding means bonded to various transparency layers when exposed to temperatures of about 120° F. and 95 percent relative humidity;

FIG. 8 is a graph showing the increased resistance to moisture permeability of mercaptan resin binding means bonded to other various transparency layers when exposed to temperatures of about 200° F. and 100 percent relative humidity;

FIG. 9 is a graph showing the composite evaluation of various interlayer binding means and the effectiveness of resistance to moisture permeability;

FIG. 10 is a cross sectional view of a transparency composite at an edge as sealed by edge sealant material of the present invention;

FIG. 11 is a cross sectional view of a transparency composite having no interlayer binding means between the intense heat resistant interlayer and the outside ply;

FIG. 12 is an illustrative view of a transparency composite having a slot to be filled and an edge sealant material;

FIG. 13 is a graph showing the variation in concentrations of the composition of the present invention and its effect on modulus stability during humidity exposure;

FIG. 14 is a graph showing the variation in concentrations of the composition of the present invention and its effect on ultimate strength stability during humidity exposure;

FIG. 15 is a cross sectional view of the transparency composite having an intense heat resistant interlayer having a chlorophosphate compound;

FIG. 16 is a graph showing the relationship between the concentration of the phosphate compound and the ability of the heat resistant interlayer to resist flame penetration.

BEST MODE FOR CARRYING OUT THE INVENTION

Transparencies that have been produced with epoxy resins desiring to achieve heat resistant properties have typically included a boroxine such as trimethoxyboroxine. Typical epoxy resins include, but are not limited to, bisphenol-A type, bisphenol-F type, and novolac type epoxy resins. Typical boroxines include boroxines having the formula ##STR6## where R is a compound having from 1 or 2 to 18 carbon atoms. Desirably, R, is an alkyl compound and has from 1 or 2 to 5 carbon atoms. Trimethoxyboroxine is preferred. Trimethoxyboroxine has exhibited, in combination with epoxy resin, a resistance to heat from a general or point source up to temperatures of 2000° F. However, a major complication is the low concentration of trimethoxyboroxine in the epoxy resin system. Previously, for large casting purposes, it was possible to use a concentration of trimethoxyboroxine of 5-7.5 parts per hundred parts of epoxy resin (PHR). Any greater concentration would deleteriously promote the reaction between the trimethoxyboroxine and epoxy resin, resulting in a short gel time making it extremely impractical to cast large panels.

It has been found that higher concentrations of a boroxine such as trimethoxyboroxine can be incorporated into an epoxy resin system and still have sufficient time to cast large sheets if a phenyl substituted alkyl alcohol is added. The alkyl alcohol contains from 1 to 20 carbon atoms and desirably from 1 to 10 carbon atoms. Preferably, benzyl alcohol is used. The alcohol acts as retarder and inhibitor for the trimethoxyboroxine epoxy reaction, permitting the usage of an increased concentration of the trimethoxyboroxine and a concommitant increase in heat resistant properties. This concentration may be readily increased to 30 parts of a boroxine such as trimethoxyboroxine per hundred parts of epoxy resin. Not only is the rate of reaction between the trimethoxyboroxine and epoxy resins inhibited, but the maximum exotherm is significantly reduced with the phenyl substituted alkyl alcohol addition, as shown in FIG. 4.

                  TABLE 1                                                          ______________________________________                                         THE EFFECT OF BENZYL ALCOHOL                                                   ON MAXIMUM EXOTHERM                                                                           Curve                                                                          2      3      4                                                 ______________________________________                                         Trimethoxyboroxine                                                                              10       10     10                                            Benzyl Alcohol    2        3      4                                            Dow DEN-431      85       85     85                                            Neopentyl Glycol                                                               Diglycidyl Ether 15       15     15                                            Gel Time (Minutes)                                                                              65       85     No sharp                                                                       gel time                                      Maximum Exotherm (°F.)                                                                   270      215    115                                           ______________________________________                                    

While phenyl substituted alkyl alcohols permit increased concentration of the trimethoxyboroxine in the epoxy resin, benzyl alcohol is preferred. Benzyl alcohol is preferred because of its purity, as well as its index of refraction, its clear color, its high flash point, its relatively low solubility in water, its low viscosity, and its high boiling point.

Both the epoxy resins capable of serving as the matrix for the intense heat resistant composite and the trimethoxyboroxine and their heat resistant properties are known to those skilled in the art of composite transparency production. However it is the inclusion of the phenyl substituted alkyl alcohol which enables one to increase the level of trimethoxyboroxine which results in an increase in intense heat resistance for the transparency not otherwise present. The phenyl substituted alkyl alcohol is present in a concentration of from about 20 parts to about 50 parts per one hundred parts of trimethoxyboroxine or from about 1 part to about 10 parts per 100 parts of epoxy resin. Preferably, the concentration of benzyl alcohol is 33 parts to one hundred parts of trimethoxyboroxine, or 3.3 parts to one hundred parts of epoxy resin.

Referring now to FIG. 1, it may be seen that the transparency composite, generally referred to as 10, is composed of three layers with the epoxy resin interply 20, a reaction product of an adduct of trimethoxyboroxine and benzyl alcohol with an epoxy resin placed between an inside ply 40 and an outside ply 30. The outside ply 30 may be composed of transparent materials well known to those skilled in the art and specifically providing impact, ballistic, abrasion, weather resistant and light reflectant resistant properties which resin interply 20 complements.

Typically, this outside ply 30 may be composed of acrylic, polycarbonate, polyurethane and any inside ply 40 may be chosen from those same transparent materials or others well known to those skilled in the art which are not necessary for impact, ballistic, abrasion, weather resistant or light reflection resistance.

All of the components of interply 20 are mixed and degassed, then cast against an acrylic ply through the use of a casting cell technique well known to individuals in the industry. Should it be necessary to cast interply 20 by itself, the same technique can be used, the only difference being interply 20 would be cast against a chemically treated glass plies, such that after cure the glass plies can be removed, resulting in an optically clear interply 20. This interply casting can then be bonded to other transparent layers with materials as discussed below. However, the use of the alcohol permits larger castings then previously possible. Gel times are increased by the addition of the alcohol to permit larger castings, as may be seen in FIG. 3.

When joining the various plies 20, 30 and 40 of the transparency composite 10, it may be necessary to use binding means to insure adequate contiguity between the various layers. For example, binding means 45 may exist between the intense heat resistant resin interply 20 and inside ply 40, and this binding means 45 may be chosen from adhesives such as silicones, urethanes and epoxies. Also, binding means 35 may be necessary between intense heat resistant resin interply 20 and outside ply 30, the composition of such binding means being typically silicones, urethanes, and epoxies.

However, it is preferred to utilize a mercaptan resin for binding means 35 and 45, as described below, to increase resistance to moisture permeability for transparency composite 10.

The intense heat resistant resin interply 20 may optionally be composed of an epoxy resin cured with adducts of a boroxine such as trimethoxyboroxine, phenyl substituted alkyl alcohols, and organic phosphorous compounds selected from the following formula: ##STR7## Where R₃ is selected from the group consisting of hydrocarbon radicals having from 1 to 24 carbon atoms, halo-substituted organic radicals having from 1 to 24 carbon atoms, and multihalo-substituted organic radicals having from 1 to 24 carbon atoms; and where R₃ may be the same or different radicals.

The R₄ is selected from the group consisting of all the radicals of R₃, oxygen, and radicals of the formula: --O--R₆, wherein R₆ is selected from the group consisting of all the radicals of R₃, organo-phosphorus polymeric radicals, and organo-phosphorus esters; where R₅ is selected from the group consisting of hydrogen, hydroxyl, oxygen, sulfur, halogens or no radical at all; and where Z is selected from the group consisting of oxygen, sulfur, or no radical at all. Examples of R₃ are phenyl, alkyl-substituted phenyl, chloro-substituted alkyl, and alkyl radicals. Examples of R₄ radicals are the examples of R₃ radicals, oxygen, phenoxy, alkyl-substituted phenoxy, alkoxy, alkyl-substituted alkoxy, chloro-substituted phenoxy, chloro-substituted alkoxy radicals and radicals having phosphorus units in polymeric or ester configuration.

Specific compounds include triphenyl phosphite, diphenyl phosphite, diphenyl isodecyl phosphite, tris nonylphenyl phosphite, tri(beta, beta' dichloroisopropyl) phosphate, tri(beta chloroethyl) phosphate, bis chloroethyl phosphate ester, and a phosphate polymer of the formula: ##STR8## where n is a number from 1 to 20.

The desirable phosphite compounds are: diphenyl phosphite, trisnonylphenyl phosphite, triphenyl phosphite, diphenylisodecyl phosphite, diphenylisooctyl phosphite and phenyldiisodecyl phosphite. Preferably, diphenyl phosphite and triphenyl phosphite may be used. The addition of from 20 parts to 400 parts of an organic phosphorous compound such as per 100 parts of the epoxy resin dramatically increases the intense heat resistant properties of the interply 20 at high temperatures, typically greater than 2000° F. Alternately, the concentration of the organic phosphorus compound may be from about 50 parts to 250 parts per 100 parts of the boroxine or from about 5 parts to about 40 parts per 100 parts of the epoxy resin. The addition of this amount of triphenyl phosphite provides sufficient phosphorus in the resin to increase the time of burn-through of a 1/4 inch casting of interply 20 almost ten times as long as interply 20 without phosphorus is further beneficial by providing a greater than 20 percent increase in time of burning at the lower temperatures around 2000° F. Therefore, the inclusion of this phosphite significantly increases the intense heat resistant properties already present in the interlayer 20 and complements the other resistant properties in outer layer 30 in the transparency composite 10.

Of the phosphate compounds, the specific phosphate compounds already mentioned are desirable. Preferably, tri(beta, beta' dichloroisopropyl) phosphate and tri(beta chloroethyl) phosphate may be used. The former is commercially available under the trade name Fyrol FR-2 manufactured by Stauffer Chemical Company, whereas the latter compound is commercially available as Fyrol CEF, manufactured by Stauffer Chemical Company. The addition of from about 10 parts to about 400 parts of the phosphate compound per 100 parts of the boroxine compound or from about 1 part to about 40 parts per 100 parts of the epoxy resin dramatically increases the intense heat resistant properties of the interply 20, as seen in FIG. 15, at high temperatures, typically greater than 2000° F.

Alternately, the concentration of the phosphate compound may be from about 50 parts to 250 parts per 100 parts of the boroxine or from about 5 parts to about 30 parts per 100 parts of the epoxy resin. The addition of this amount of the preferred chlorophosphate compounds described above provides sufficient phosphorus in the resin to increase the time of burn-through of a casting of interply 20, as seen in FIG. 16 and the following tables.

A comparison of the phosphate compound with the phosphite compound demonstrates the preference of the phosphate compounds. In the production of the phosphite compounds, trace amounts of water are impurities which generate the production of phenol during the curing of the interply 20. The generation of free phenol accelerates gel times which must be retarded as seen in FIG. 4 to permit larger castings. Substitution of the phosphate compound for its synergistic heat resistant properties into interply 20 avoids the presence of water impurities in the phosphite compounds, which permits a control over the gel time of the larger castings. Further, the phosphate compound does not shorten gel times because the chemical interaction of the phosphate during curing does not produce byproducts which act as accelerators for the reaction. As the optimum phosphate compound concentration is obtained, it may be possible to eliminate the phenol substituted alkyl alcohol as an inhibitor of gel time, such as that seen in FIG. 3. The following Table 2 demonstrates the formulation of an interply 20 employing phosphate compounds. However, it may be possible to employ a combination of phosphite and phosphate compounds for improved burn-through efficiency.

                                      TABLE 2                                      __________________________________________________________________________     FORMULATIONS OF INTERPLY 20 USING PHOSPHITE AND                                PHOSPHATE COMPOUNDS, RESPECTIVELY/IMPROVEMENT IN HEAT RESISTANCE               __________________________________________________________________________                1   2  3   4   5   6   7   8   9                                    __________________________________________________________________________     Boroxine Compound                                                                         10  10 10  10  10  10  10  10  10                                   (trimethoxyboroxine)                                                           Phenyl Substituted                                                                         3   3 3    3   3  3    3   3  3                                    Alkyl Alcohol                                                                  (benzyl alcohol)                                                               Novolac-Type Epoxy                                                                        90  90 90  45  45  45  --  --  --                                   Resin (DEN-431)                                                                Bisphenol-F Type                                                                          --  -- --  45  45  45  90  90  90                                   Epoxy Resin                                                                    (EPICLON-830)                                                                  Phosphite Compound                                                                        10  -- 5   10  --  5   10  --  5                                    (triphenyl phosphite)                                                          Phosphate Compound                                                                        --  10 5   --  10  5   --  10  5                                    (Fyrol CEF)                                                                    Silane Compound                                                                            1   1 1    1   1  1    1   1  1                                    (A-187)                                                                        Burn-through time                                                                         1.6 1.6                                                                               1.5 1.9 1.9 1.8 2.4 2.2 2.0                                  at approximately                                                               6000° F. (sec.)                                                         Percentage change                                                                         control                                                                             0%                                                                               -6% +19%                                                                               +19%                                                                               +13%                                                                               +50%                                                                               +38%                                                                               +25%                                 in heat resistance                                                             __________________________________________________________________________                             10  11  12  13  14 15                                  __________________________________________________________________________                  Boroxine Compound                                                                         10  10  10  10  10 10                                               (trimethoxyboroxine)                                                           Phenyl Substituted                                                                        --  --  --  --  -- --                                               Alkyl Alcohol                                                                  (benzyl alcohol)                                                               Novolac-Type Epoxy                                                                        --  --  --  --  -- --                                               Resin (DEN-431)                                                                Bisphenol-F Type                                                                          90  90  90  90  90 90                                               Epoxy Resin                                                                    (EPICLON-830)                                                                  Phosphite Compound                                                                        --  --  --  --  -- --                                               (triphenyl phosphite)                                                          Phosphate Compound                                                                        --  10  15  20  25 30                                               (Fyrol CEF)                                                                    Silane Compound                                                                           --  --  --  --  -- --                                               (A-187)                                                                        Burn-through time                                                                         2.0 3.0 3.0 3.0 2.0                                                                               2.0                                              at approximately                                                               6000° F. (sec.)                                                         Percentage change                                                                         control                                                                            +50%                                                                               +50%                                                                               +50%                                                                                0%                                                                                0%                                              in heat resistance                                                __________________________________________________________________________

As may be seen by reference to Table 2, variations of the formulations 1-9 demonstrate the substitution of the phosphate compound in interply 20 compared with a phosphite compound in interply 20. When coupled with the reaction processing advantages of the phosphate compound, the substitution of the phosphate compound for the phosphite compound is desirable. Therefore, the use of interply 20 having phosphate compounds therein for any heat resistant interlayer 20 in any laminate described herein is possible and within the concept of this invention. Testing for formulations 1-9 for burn-through time at approximately 6000° F. was conducted with a laminate structure identified in FIG. 15 where plies 30 and 40 were acrylic.

An examination of formulations 10-15 in Table 2, in comparison with FIG. 16 demonstrates the ability of an interply 20 having a phosphate compound to resist the preparation of high heat sources. Formulations 10-15 demonstrate an increasing concentration of the phosphate compound from a control having no phosphate to an interply 20 having 30 parts by weight of phosphate compound. As seen in FIG. 16, three samples of each formulation was exposed to a heat source developing temperatures at about 6000° F. The reciprocal of penetration in inches demonstrates the resistance of each formulation to exposure time in seconds. Consequently, it is apparent that an optimal concentration of the phosphate ranges between about 10 parts by weight to about 20 parts by weight. Indeed, formulations 11-13 were capable of withstanding exposure times for a period of about three seconds which exceeds the burn-through time for any of the formulations 1-9. Therefore, it is optimal to have from about 10 to about 20 parts of the phosphate compound in interply 20. Again, testing of interply 20 occurred using a laminate seen in FIG. 15 where inside and outside plies 30 and 40 respectively, were both acrylic.

Referring again to Table 2, it is also apparent that the epoxy resin may desirably be a bisphenol-F type epoxy resin. Comparison of formulations 1-3 with formulations 7-9 demonstrate a percentage change in heat resistance when the novalac-type epoxy resin is substituted with the bisphenol-F type epoxy resin.

Referring now to FIG. 2, the importance of intense heat resistant epoxy resin interply 20 in a clad composite transparency may be understood. This transparency 50 is shown cross-sectionally to demonstrate the effectiveness of a particular clad composite format. Clad outside ply 30 having binding means 35 is secured to intense heat resistant resin interply 20 comprising an epoxy resin cured with adducts of trimethoxyboroxine and benzyl alcohol alone or together with triphenyl phosphite. Alternatively, interply 20 may be cured with a boroxine compound and a phosphate compound, alone or together with a phenylsubstituted alcohol. A silicone interlayer 80 functions as a flexible adhesive to the opposite surface of interply 20 to a silicate layer 70 typically composed of soda lime glass, borosilicate glass, aluminosilicate glass, silica glass or 96 percent silica glass. On the opposite side of silicate layer 79 is an interlayer 60 which consists of a silicone or polyurethane or polyvinyl butyral interlayer. On the opposite side of interlayer 60 is a second silicate layer 70. On the opposite side of the second silicate is binding means 45 which consists of a silicone or polyurethane interlayer. On the opposite side of the binding means 45 is the inside ply 40 of the composite, composed of the same materials as discussed above, including polycarbonate.

However, it is also possible to utilize a mercaptan resin for any or all of binding means 35 and 45 and interlayers 60 and 80. The importance of such mercaptan resin in moisture permeability resistance for composite 50 is described below.

It has been found that the combination of these layers 20, 30, 35, 40, 45, 60, 70, and 80 in the order described above provides a synergistic resistance greater than the application of layers 30 and 40 surrounding interlayer 20. Clad outer layer 30 may be selected from those transparent materials commonly known to those skilled in the art, as described above and typically be acrylic.

For an understanding of the improved heat resistant properties of interply 20, reference is had to FIG. 5.

                  TABLE 3                                                          ______________________________________                                         HEAT RESISTANT TRANSPARENCIES - RELATIONSHIP                                   BETWEEN BURNTHROUGH TIME AND                                                   EXPOSURE TEMPERATURE                                                                        Line                                                                           A    B         C      D                                           ______________________________________                                         Trimethoxyboroxine                                                                            7.5    10        10   7.5                                       Benzyl Alcohol --      5         3   2.5                                       Triphenyl Phosphite                                                                           --      5        10   --                                        DER-332        100    --        --   --                                        DEN-431        --     85        90   90                                        Heloxy-68      --     15        --   --                                        Silane A-187   --      1         1    1                                        Diphenyl Phosphite                                                                            --     --        --   15                                        Burnthrough at 378    522       790  9000                                      2000° F. (secs.)                                                        Burnthrough at 0.4    3.0       3.7  5.8                                       6000° F. (secs.)                                                        ______________________________________                                    

It can be seen from FIG. 5 that by the addition of benzyl alcohol, a higher concentration of trimethoxyboroxine can be incorporated, resulting in improved, burn-through resistance at 2000° F. and at 6000° F.

Transparencies 10 and 50 which contain interply 10 may be utilized in various military and industrial applications. Typically, these applications may include the use of transparencies in military hardware and aircraft, as well as spacecraft. Further, industrial applications include transparencies where protection against the thermal effects of fossil fuel fires, nuclear blasts and high energy radiation are required.

The lasting success of any transparency composite, designed to withstand high heat resistance, impact resistance, ballistic resistance, abrasion resistance remains dependent upon its continuing transparent nature. The plurality of layers of composites 10 and 50 and the chemical composition of each layer are differentially susceptible to the permeation of moisture into and through the layers. The retention of moisture between and within the various layers of this invention and any conventional transparency composite having multiple layers creates a haze which disrupts clarity of light transmissions through the transparency composite.

A barrier to the generation of haze is necessary for any multi-layer transparency composite. The layers 35 and 45 and interlayers 60 and 80 have been found to provide the most effective permeation barrier, resistant to moisture permeability into central layers, such as heat resistant interlayer 20 and silicate layers 70 as seen in FIG. 1 and FIG. 2, or for heat resistant interlayers 20 having phosphate compounds therein.

The composition for the binding means 35 and 45 and interlayers 60 and 80 comprises about 100 parts by weight of a mercaptan terminated resin, from about 40 to about 250 parts by weight of an epoxy resin, and from about 0.5 to about 4.0 parts by weight of a silane catalyst.

The mercaptan terminated resin is an aliphatic hydrocarbon based compound having a thio reactive group terminating each end of the molecule.

The mercaptan has the following general formula: ##STR9## where R is an aliphatic hydrocarbon having from 1 to 18 carbon atoms and n is 1 or 2. The mercaptan resin is a material commercially available from Diamond Shamrock Corporation and sold identified as DION-3-800LC.

The epoxy resin of the binding means 35 or 45 or interlayer 60 or 80 is composed of epoxy resins previously disclosed with reference to interply 20. Typical epoxy resins include, but are not limited to, bisphenol-A type, bisphenol-F type, and novolac type epoxy resins. A preferred concentration of the epoxy resin depends on the type of epoxy resin used. For an epoxy-novolac type resin the preferred concentration is about 100 parts by weight. Epoxy resins commercially available include DER-332, a product of Dow Chemical Company.

The silane catalyst of the binding means 35 or 45 or interlayer 60 or 80 is composed of an amine terminated silane compound such as

N-aminoalkyl-aminoalkyl-trialkoxysilanes of the formula ##STR10## wherein R₁ is an alkylene having 1-6 carbon atoms and R₂ is an alkyl, having 1-6 carbon atoms, and

aminoalkyl-trialkoxysilanes of the formula ##STR11## wherein R₁ and R₂ are as defined above.

Examples of preferred silanes are gamma aminopropyl triethoxy silane and normal beta aminopropyl gamma aminopropyl trimethoxy silane. The preferred concentration of the amino-silane catalyst is about 2.5 parts by weight. The aminosilane is commercially available from Union Carbide in their A-1110 and A-1120 formulations.

As expressed above, the binding means 35 or 45 and interlayer 60 or 80 have traditionally employed conventional silicones, urethanes, and epoxies. However, use of the mercaptan interlayer for these purposes provides unexpected improvement to resistance to moisture permeation. The following table compares the test samples having various composite constructions, including a construction having outer ply 30, heat resistant interlayer 20, binding means 45 and inner ply 40, such as that seen in FIG. 11, and a construction having no binding means 35 or 45.

                  TABLE 4                                                          ______________________________________                                         Composite                     Thick-                                           Number    Composite Component ness (in.)                                       ______________________________________                                         1         polycarbonate (30)  0.256                                                      silicone resin (35) 0.1                                                        Heat resistant interlayer (20)                                                                     0.236                                                      silicone resin (45) 0.1                                                        polycarbonate (40)  0.256                                            2         polycarbonate (30)  0.256                                                      mercaptan interlayer (35)                                                                          0.1                                                        heat resistant interlayer (20)                                                                     0.236                                                      mercaptan interlayer (45)                                                                          0.1                                                        polycarbonate (40)  0.256                                            3         as-cast acrylic (30)                                                                               0.125                                                      heat resistant interlayer (20)                                                                     0.236                                                      as-cast acrylic (40)                                                                               0.125                                            4         as-cast acrylic (30)                                                                               0.125                                                      heat resistant interlayer (20)                                                                     0.236                                                      silicone resin (45) 0.1                                                        polycarbonate (40)  0.256                                            5         as-cast acrylic (30)                                                                               0.125                                                      heat resistant interlayer (20)                                                                     0.236                                                      mercaptan layer (45)                                                                               0.1                                                        polycarbonate (40)  0.256                                            6         stretched acrylic (30)                                                                             0.1                                                        heat resistant interlayer (20)                                                                     0.125                                                      stretched acrylic (40)                                                                             0.1                                              7         urethane (30)       0.1                                                        heat resistant interlayer (20)                                                                     0.236                                                      urethane (40)       0.1                                              8         urethane (30)       0.1                                                        silicone resin (35) 0.1                                                        heat resistant interlayer (20)                                                                     0.236                                                      silicone resin (45) 0.1                                                        urethane (40)       0.1                                              9         urethane (30)       0.1                                                        mercaptan interlayer (35)                                                                          0.1                                                        heat resistant interlayer (20)                                                                     0.236                                                      mercaptan interlayer (45)                                                                          0.1                                                        urethane (40)       0.1                                              10        as-cast acrylic (30)                                                                               0.08                                                       heat resistant interlayer (20)                                                                     0.236                                                      as-cast acrylic (40)                                                                               0.08                                             11        as-cast acrylic (30)                                                                               0.1                                                        silicone resin (35) 0.1                                                        heat resistant interlayer (20)                                                                     0.236                                                      silicone resin (45) 0.1                                                        as-cast acrylic (40)                                                                               0.1                                              12        as-cast acrylic (30)                                                                               0.08                                                       mercaptan interlayer (35)                                                                          0.1                                                        heat resistant interlayer (20)                                                                     0.236                                                      mercaptan interlayer (45)                                                                          0.1                                                        as-cast acrylic (40)                                                                               0.08                                             ______________________________________                                    

The composites of Table 4 were tested under extreme temperature and humidity conditions. The direct comparison of the performance of the mercaptan resin of the present invention and the preformance of the conventional silicone resin, or no binding means at all, may be seen in the graphs of FIGS. 6-9.

In FIG. 6, the percent of haze occurring in the composite is compared with days of constant exposure of the composite at 200° F. and 100 percent relative humidity. All other parameters constant, a direct comparison of composite No. 2 with the mercaptan interlayer of the present invention demonstrates the increased resistance to moisture permeation in the latter composite. Likewise, a direct comparison of composites No. 4 and No. 5 show the increased resistance to moisture permeation in the latter composite. Composites No. 2 and No. 5 are clearly superior to their counterparts No. 1 and No. 4, as well as No. 3 and No. 6 which do not provide any binding means moisture permeation protection.

In FIG. 7, a graph showing the effect of constant exposure to 120° F. and 95 percent relative humidity to the same six composites is seen. While not as pronounced as that seen in FIG. 6, the comparison of composites No. 1 and No. 2 and of composites No. 4 and No. 5 clearly indicates the superiority of the mercaptan interlayer binding means over the silicone resin binding means.

In FIG. 8, the graph showing the test of exposure at 200° F. and 100 percent relative humidity for the remaining six composites is seen. A direct comparison of composites No. 8 and No. 9, where the only difference is the substitution of mercaptan interlayer for silicone resin, demonstrates the clear superiority of the mercaptan resin in resistance to haze as caused by moisture permeation. Further, a comparison of composites No. 11 and No. 12, substituting mercaptan interlayer for silicone resin, demonstrates the superiority of the mercaptan interlayer of the present invention over conventional binding means.

FIG. 9 summarizes the superiority of the mercaptan interlayer of the present invention over conventional or no resin by comparing performance at 200° F./100% relative humidity with performance at 120° F./95% relative humidity. At identical acceptable percentage haze levels, the mercaptan interlayer could last as long as 100 days at 120° F./95% relative humidity and 35 days at 200° F./100% relative humidity. By comparison, the silicone resin could only withstand about 22 days at 120° F./95% relative humidity and 8 days at 200° F./100% relative humidity.

FIGS. 6-8 also demonstrate that the mercaptan interlayer of the present invention is effective for conventional outer and inner plies 30 and 40: acrylic, polycarbonate, urethane, and any combinations of them. Moreover, the mercaptan interlayer is available to replace the conventional silicone, epoxy, or urethane resins for any transparency composite using any conventional transparency including silicates commonly known as glass. Indeed, the mercaptan interlayer of the present invention is an effective interlayer 60 and 80 for clad composite transparency 50 as seen in FIG. 2.

Table 5 below demonstrates a comparison of the specific permeability values for various formulations of the mercaptan interlayer and the conventional silicone and other resins. The specific permeability of a film to moisture is defined as the milligrams of water that permeate one square centimeter of film of 1 millimeter thickness each 24 hours after a constant rate has been attained under the preferred conditions of 25° C. and using 100% relative humidity inside the cup and a phosphorus pentoxide desiccated atmosphere outside the cup. The formula of calculation is ##EQU1## where SP is specific permeability, W is weight loss in milligrams in a 24 hour period, T is the film thickness in inches, and A is exposed cup surface area.

                  TABLE 5                                                          ______________________________________                                                          Film    Specific                                                               Thick-  Permeability.sup.4                                    Type of Resin    ness    (ASTM D-1632-62)                                      ______________________________________                                         mercaptan interlayer.sup.1                                                                      0.098   0.4978                                                mercaptan interlayer.sup.2                                                                      0.124   0.0627                                                mercaptan interlayer.sup.3                                                                      0.114   0.4633                                                low-strength silicone                                                                           0.100   4.8539                                                low-strength RTV sili-                                                         cone             0.104   4.2270                                                high-strength silicone                                                                          0.100   4.8768                                                high-strength RTV sili-                                                        cone             0.118   5.4549                                                pigmented RTV silicone                                                                          0.101   4.0020                                                ______________________________________                                          .sup.1 Mercaptan interlayer comprising 100 parts by weight of mercaptan        resin, 100 parts by weight of epoxy resin, and 2 parts by weight of silan      catalyst.                                                                      .sup.2 Mercaptan interlayer comprising 100 parts by weight of mercaptan        resin, 50 parts by weight of epoxy resin, and 1.5 parts by weight of           aminosilane catalyst.                                                          .sup.3 Mercaptan interlayer comprising 100 parts by weight of mercaptan        resin, 100 parts by weight of epoxy resin, and 1 part by weight of             aminosilane catalyst.                                                          .sup.4 Units in mg. mm/24 hr. cm.sup.2.                                  

Because the ideal specific permeability is near zero, it is readily seen that a mercaptan interlayer of the present invention is approximately 10 times better than conventional resins. This direct comparison demonstrates the vast superiority of a mercaptan interlayer of the present invention over those binding agents presently employed.

Two other properties significant for the interlayer of the present invention are ultimate strength and modulus. During high temperature, high humidity condition, the interlayer must maintain proper adhesion to prevent delamination of the interlayer and the other various layers in the composite. Further, the interlayer must have an acceptable rate of change of modulus during the high temperature, high humidity conditions, to prevent alteration of the interlayer effectiveness sandwiched between other layers during the course of use. For a comparison of modulus and ultimate strength properties of the interlayers of the present invention with interlayers common to those skilled in the art, reference is had to Tables 6 and 7. Table 6 describes the formulation of the testing material and Table 7 demonstrates the effect of high temperature and high humidity on the modulus and ultimate strength properties of the formulations.

                  TABLE 6                                                          ______________________________________                                         FORMULATION OF INTERLAYER FOR COMPOSITE                                        OF GLASS - INTERLAYER - POLY CARBONATE                                                Mercap-                 High   Fumed                                    Formu- tan      Epoxy   Amino- Strength                                                                              Silica                                   lation Resin    Resin   Silane Silicone                                                                              Compound 1                               ______________________________________                                         1      100      100     2      --     --                                       2      100      150     2      --     --                                       3      100      175     2      --     --                                       4      100      200     3      --     --                                       5      --       --      --     100    5                                        6      --       --      --     100    --                                       ______________________________________                                           *1 A thixotropic agent available commercially as CABO-SIL EH5.          

                                      TABLE 7                                      __________________________________________________________________________               Torsional - Shear Modulus/Ultimate                                             Strength (PSI)                                                                 Formulation                                                                    1    2   3    4    5   6                                             __________________________________________________________________________     Days of                                                                               1  210/771                                                                             78/148                                                                             25/62                                                                               28/60                                                                               25/43*                                                                             16/53                                         Exposure at                                                                           2  207/450                                                                             --  22   22    6/8**                                                                             --                                            120° F./95%                                                                    3  --   --  --   --   --  22/72                                         Relative                                                                              4  --   --  --   --   --    7/19**                                      Humidity                                                                              6  190/291                                                                             49/110                                                                             --   33/67                                                                               6/10                                                                               --                                                   7  --   --  33/65                                                                               --   --  --                                                   14 166/266                                                                             73/122                                                                             --    98/153                                                                             9/14                                                                               --                                                   15 --   --   55/101                                                                             --   --  --                                                   27  85/200                                                                             --  --   105/289                                                                             --  --                                            __________________________________________________________________________      *Haze Appeared                                                                 **Delamination Started                                                   

As may be seen from an examination of Table 7, a variation in the formulation of the inner layer of the present invention may control the modulus and its rate of change during the days of exposure to high-temperature/high-humidity conditions. Over the course of the period examined, the ultimate strength and its rate of change could be controlled by the type of formulation of the interlayer. Generally, with increasing epoxy resin concentration, the modulus and ultimate strength comparisons during the days of the exposure increased when the epoxy was greater than 150 parts per 100 parts of mercaptan resin.

Table 7 also demonstrates the clear superiority of the interlayer formulations of the present invention over those interlayer compositions known to those skilled in the art. On the first day, formulation No. 5 exhibited haze, and by the fourth day, both silicone formulations started to delaminate from the composite of glass-interlayer-polycarbonate. In comparison to this, the formulations 1 and 4 lasted as long as 27 days when the experiment was concluded to report these results. Furthermore, the interlayer formulations of the present invention have a variety of modulus and ultimate strength properties to meet various commercial applications depending upon the materials between which the interlayer is sandwiched.

From an examination of FIGS. 13 and 14, it is possible to optimize the formulation for modulus stability and ultimate strength stability. FIG. 13 demonstrates in graphic form the information shown in Table 6 for a comparison of initial modulus with the modulus after 14 days of exposure. A ratio of epoxy resin/mercaptan resin exhibits stability over the 14 days in the range of 1.5 to 1.8. Likewise, this ratio is confirmed for ultimate strength comparisons as seen in FIG. 14.

The mercaptan composition of the present invention is effective, not only to resist moisture permeation between plies of transparent composite construction. As seen in FIG. 10, edge sealant 95 may seal edges of outer ply 30, heat resistant interlayer 20, binding means 45 (either of the invented composition or a conventional composition) and the upper surface of inner layer 40. The composite shown in FIG. 10 is the same as the composite 90 shown in FIG. 11, typical of transparent composites used in high elevation aircraft. Edge sealer 95 is likewise useful to seal edges of composites 20 and 50 shown in FIG. 2 or any conventional transparent composite, either with inner ply 40 extending beyond the other transparency components or cut at the same place as the other transparency components.

The mercaptan composition may also fill in the slot created during the manufacture of the transparency on the outside edge of any transparency composite. As seen in FIG. 12, this slot filler 105 combines the functions of the edge sealant 95 and the interlayer 45. Neither the slot filler 105 nor the edge sealant need be transparent and may be translucent or opaque with the addition of thixotropic agents, such as fumed silica compounds, or fillers. Indeed, slot filler 105 and edge sealer 95 may merge into a perimeter sealant.

The edge sealer 95 and the slot filler 105 demonstrates significant improvements over the use of high-strength silicones known to those skilled in the art. An examination of Table 8 demonstrates the moisture impermeability of the mercaptan compositions over that of the high-strength silicone.

                                      TABLE 8                                      __________________________________________________________________________     EXAMINATION OF GLASS-SILICONE-POLYCARBONATE COMPOSITES WITH                    EDGE SEALERS AND SLOT FILLERS EXPOSED 29 DAYS AT 120° F./95% R.H.                PANEL NO. 1                                                                            PANEL NO. 2                                                                             PANEL NO. 3                                                                             PANEL NO. 4                                                                             PANEL NO. 5                        __________________________________________________________________________     SLOT-    HIGH-STRENGTH SILICONE    MERCAPTAN*                                                                              MERCAPTAN**                        FILLER                             COMPOSITION                                                                             COMPOSITION                        (105)    PLUS 5% BT WT.            PLUS 5% BY WT.                                                                          BLUS 5% BY WT.                              CAB-O-SIL EH-5            CAB-O-SIL EH-5                                                                          CAB-O-SIL EH-5                              (Fumed Silica Compound)   (Fumed Silica                                                                           (Fumed Silica Compound                                                Compound)                                   EDGE     NONE    MERCAPTAN                                                                               MERCAPTAN                                                                               MERCAPTAN                                                                               MERCAPTAN                          SEALER           COMPOSITION*                                                                            COMPOSITION**                                                                           COMPOSITION*                                                                            COMPOSITION**                      (95)             PLUS 5% BY WT.                                                                          PLUS 5% BY WT.                                                                          PLUS 5% BY WT.                                                                          PLUS 5% BY WT.                                      CAB-O-SIL EH-5                                                                          CAB-O-SIL EH-5                                                                          CAB-O-SIL EH-5                                                                          CAB-O-SIL EH-5                                      (Fumed Silica                                                                           (Fumed Silica                                                                           (Fumed Silica                                                                           (Fumed Silica Compound)                             Compound)                                                                               Compound)                                                                               Compound)                                   INTERLAYER                                                                              Slot-Filler                                                                            Edge sealer cut                                                                         Edge sealer cut                                                                         Edge sealer cut                                                                         Edge sealer cut                    (HIGH-   can be removed                                                                         off      off      off      off                                STRENGTH         Slot-Filler could                                                                       Slot-Filler could                                                                       Slot-Filler                                                                             Slot-Filler had                    SILICONE)        be removed with                                                                         be remove with                                                                          could by removed                                                                        to by dug out                      (45)             manual difficulty                                                                       difficulty                                                                              with difficulty                                      Silicone inter-                                                                        Silicone inter-                                                                         Silicone inter-                                                                         Silicone inter-                                                                         Silicone inter-                             layer can be                                                                           layer could be                                                                          layer could by                                                                          layer appeared                                                                          layer appeared                              readily delam-                                                                         delaminated from                                                                        delaminated from                                                                        to be well                                                                              to be well                                  inated from                                                                            both, The adhe-                                                                         glass only-was                                                                          bonded   bonded - minor                              glass and poly-                                                                        sion was much                                                                           better than Panel spot delaminations                          carbonate                                                                              better than Panel                                                                       No. 1                                                                 No. 1                                                         __________________________________________________________________________      *Mercaptan Resin 100 Epoxy Resin 100 AminoSilane 2                             **Mercaptan Resin 100 Epoxy Resin 200 AminoSilane 2                      

Each panel was subjected to 29 days of exposure at 120° F. and 95% relative humidity. Panel No. 1 only had a high-strength silicone slot filler and once that was removed, it was apparent that the silicone interlayer could be readily delaminated from both the glass and the polycarbonate layers. In contrast to this the mere addition of an edge sealer having one mercaptan composition plus the thixatropic agent increase the performance of the composite during the 29 days of exposure. After the edge sealer 95 was cut off, the slot filler 105 could only be removed with manual difficulty. However, the silicone interlayer could be delaminated from both the glass and polycarbonate, although the adhesion was better than that found in Panel 1. By increasing the epoxy resin concentration, Panel 3 demonstrated some improvement over that seen for Panel 2. In this case, after the edge sealer and slot filler were cut off and removed with manual difficulty, the silicone interlayer could be delaminated from only the glass layer. While Panels 2 and 3 represent improvement over the conventional performance of Panel 1, Panels 4 and 5 provide even greater improvement.

By using the mercaptan compositions for both slot filler 105 and edge sealer 95, the interlayer was significantly protected from moisture permeation. For the interlayers of Panels 4 and 5, the combination of the edge sealer and slot filler provided the protection to maintain a bond between the silicone interlayer and both the glass and polycarbonate. Indeed, using this second mercaptan composition, slot filler 105 had to be dug from the periphery of the Panel No. 5.

The mercaptan compositions of the present invention not only serve as an interlayer, but also may serve as an edge sealer or slot filler. The variety of combinations of transparent composites which may employ the composition of the present invention in these various functions is within the scope of this invention.

While in accordance with the Patent Statutes, one best mode and preferred embodiment of the invention has been provided, the invention is not to be limited thereto or thereby. Therefore, for an understanding of the scope of the invention, reference is had to the following claims: 

What is claimed is:
 1. A transparent composition curable to a product having resistance to intense heat, comprising: p1 a transparent blend having(a) from about 80 to about 100 parts by weight of an epoxy resin; (b) from about 5 to about 30 parts by weight of a boroxine having the formula: ##STR12## where R is a compound having from 1 to 18 carbon atoms, and (c) from about 1 part to about 40 parts by weight of an organic phosphorus compound having the following formula: ##STR13## where R₃ is selected from the group consisting of hydrocarbon radicals having from 1 to 24 carbon atoms, halo-substituted organic radicals having from 1 to 24 carbon atoms, and multihalo-substituted organic radicals having from 1 to 24 carbon atoms; and where R₃ may be the same or different radicals where R₄ is selected from the group consisting of all the radicals of R₃, oxygen, and radicals of the formula: --O--R₆, where R₆ is selected from the group consisting of all the radicals of R₃, organo-phosphorus polymeric radicals, and organo-phosphorus esters; where R₅ is selected from the group consisting of hydrogen, hydroxy, oxygen, sulfur, halogens or no radical at all; and where Z is selected from the group consisting of oxygen, sulfur, or no radical at all.
 2. A transparent composition curable to a product having resistance to intense heat, according to claim 1, wherein said transparent blend further has from about 1 part to about 10 parts by weight of a phenyl substituted alkyl alcohol, said alkyl alcohol having from 1 to 20 carbon atoms.
 3. A transparent composition curable to a product having resistance to intense heat, according to claim 2, wherein R of said boroxine is an alkyl compound having from 1 to 5 carbon atoms; andwherein said alkyl alcohol has from 1 to 10 carbon atoms.
 4. A transparent composition curable to a product having resistance to intense heat, according to claim 3, wherein said boroxine comprises about 10 parts by weight; andwherein said phenyl substituted alkyl alcohol comprises about 3 parts by weight.
 5. A transparent composition curable to a product having resistance to intense heat, according to claim 2, wherein said transparent blend further comprises from about 1 part to about 40 parts by weight of a phosphite compound selected from the group consisting of diphenyl phosphite, trisnonylphenyl phosphite, triphenyl phosphite, diphenylisooctyl phosphite, phenyl diisodecyl phosphite, diphenylisodecyl phosphite, and combinations thereof.
 6. A transparent composition curable to a product having resistance to intense heat, according to claim 1, wherein said organic phosphorus compound is a phosphate compound having the following formula: ##STR14## where R₃ and Z are the same radicals as defined in claim 1 and R₄ is selected from the group of radicals consisting of phenoxy, alkyl-substituted phenoxy, alkoxy, alkyl-substituted alkoxy, chloro-substituted phenoxy, and chloro-substituted alkoxy.
 7. A transparent composition curable to a product having resistance to intense heat, according to claim 6, wherein said phosphate compound has the following formula: ##STR15## where R₃ and R₄ are the same radicals as defined in claim
 6. 8. A transparent composition curable to a product having resistance to intense heat, according to claim 7, wherein said phosphate compound is selected from the group consisting of: tri(beta, beta' dichloroisopropyl)phosphate, tri(betachloroethyl) phosphate, and combinations thereof.
 9. A transparent composition curable to a product having resistance to intense heat, according to claim 1, wherein said organic phosphorus compound comprises from about 5 to about 35 parts by weight.
 10. A transparent composition curable to a product having resistance to intense heat, according to claim 9, wherein said organic phosphorus compound comprises from about 10 to about 20 parts by weight.
 11. A transparent composition curable to a product having resistance to intense heat, according to claim 1, wherein said epoxy resin comprises a bisphenol-F type epoxy resin. 